Evaluation of the Effect of the Addition of Hydroxyapatite on Selected Mechanical and Tribological Properties of a Flow-Type Composite.

(1) Background: The aim of the study was to determine the effect of modification with sintered hydroxyapatite (HAp) on selected mechanical and tribological properties of a flow-type composite. (2) Methods: Samples in the shapes of cuboidal beams ( n = 120) and cylinders ( n = 120) with the proper dimensions were prepared from a standard flow-type composite and others with the addition of 2% wt., 5% wt., and 8% wt. sintered hydroxyapatite. The bending strength, compression strength, diametral compression strength, impact resistance, hardness, and tribological properties were compared. (3) Results: In all cases, it was established that an increase in the amount of HAp caused a reduction in the bending, compression, and diametral compression strength. Increasing the amount of added HAp also reduced the impact strength, hardness, and wear resistance. However, the differences were statistically insignificant. (4) Conclusions: The addition of hydroxyapatite to a flow-type composite material worsened its mechanical and tribological properties; however, the obtained values were acceptable with 2% wt. and 5% wt. HAp.