Correlation between Friction and Wear in Cylindrical Anchorages Simulated with Wear Machine and Analyzed with Scanning Probe and Electron Microscope.

This paper presents the possibilities of applying atomic force microscopy (AFM) techniques to the study of the wear of prosthetic biomaterials. In the conducted research, a zirconium oxide sphere was used as a test piece for mashing, which was moved over the surface of selected biomaterials: polyether ether ketone (PEEK) and dental gold alloy (Degulor M). The process was carried out with constant load force in an artificial saliva environment (Mucinox). An atomic force microscope with an active piezoresistive lever was used to measure wear at the nanoscale. The advantage of the proposed technology is the high resolution of observation (less than 0.5 nm) in the three-dimensional (3D) measurements in a working area of 50 × 50 × 10 µm. The results of nano wear measurements in two measurement setups are presented: zirconia sphere (Degulor M and zirconia sphere) and PEEK were examined. The wear analysis was carried out using appropriate software. Achieved results present a tendency coincident with the macroscopic parameters of materials.