Microstrain and Urbach Energy Relaxation in FAPbI 3 -Based Solar Cells through Powder Engineering and Perfluoroalkyl Phosphate Ionic Liquid Additives.

Structural and electronic imperfections are the origin of defects and lead to nonradiative recombination that is detrimental to fabricating efficient perovskite solar cells. Here, we propose a powder engineering methodology for α-FAPbI 3 as a precursor material. Our developed methodology of α-FAPbI 3 synthesis mitigates the notorious structural and electronic imperfections evidenced by a significant decline in the microstrain and Urbach energy as compared to reported δ-FAPbI 3 powder and conventional precursor routes. In addition to the performance enhancement in photovoltaics, our engineered powder showed remarkable thermal and moisture stability along with cost-effectiveness through the employment of low-grade PbI 2 . Further, through additive engineering, with the use of ultrahydrophobic perfluoroalkyl phosphate anion-based ionic liquids, the microstrain and Urbach energy achieved the lowest values of 1.67 × 10 -4 and 12.47 meV, respectively, as a result of defect passivation and a semi-ionic F-Pb interaction that stabilizes the surface.