Structural characterization of SnS crystals formed by chemical vapour deposition.
Ankit Nalin MehtaH ZhangA DabralO RichardP FaviaH BenderA DelabieM CaymaxM HoussaG PourtoisW VandervorstPublished in: Journal of microscopy (2017)
The crystal and defect structure of SnS crystals grown using chemical vapour deposition for application in electronic devices are investigated. The structural analysis shows the presence of two distinct crystal morphologies, that is thin flakes with lateral sizes up to 50 μm and nanometer scale thickness, and much thicker but smaller crystallites. Both show similar Raman response associated with SnS. The structural analysis with transmission electron microscopy shows that the flakes are single crystals of α-SnS with [010] normal to the substrate. Parallel with the surface of the flakes, lamellae with varying thickness of a new SnS phase are observed. High-resolution transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), first-principles simulations (DFT) and nanobeam diffraction (NBD) techniques are employed to characterise this phase in detail. DFT results suggest that the phase is a strain stabilised β' one grown epitaxially on the α-SnS crystals. TEM analysis shows that the crystallites are also α-SnS with generally the [010] direction orthogonal to the substrate. Contrary to the flakes the crystallites consist of two to four grains which are tilted up to 15° relative to the substrate. The various grain boundary structures and twin relations are discussed. Under high-dose electron irradiation, the SnS structure is reduced and β-Sn formed. It is shown that this damage only occurs for SnS in direct contact with SiO2 .