Canonic-Like HER Activity of Cr1- x Mox B2 Solid Solution: Overpowering Pt/C at High Current Density.
Hyounmyung ParkEunsoo LeeMing LeiHyunkeun JooSinisa CohBoniface P T FokwaPublished in: Advanced materials (Deerfield Beach, Fla.) (2020)
Abundant transition metal borides are emerging as substitute electrochemical hydrogen evolution reaction (HER) catalysts for noble metals. Herein, an unusual canonic-like behavior of the c lattice parameter in the AlB2 -type solid solution Cr1- x Mox B2 (x = 0, 0.25, 0.4, 0.5, 0.6, 0.75, 1) and its direct correlation to the HER activity in 0.5 M H2 SO4 solution are reported. The activity increases with increasing x, reaching its maximum at x = 0.6 before decreasing again. At high current densities, Cr0.4 Mo0.6 B2 outperforms Pt/C, as it needs 180 mV less overpotential to drive an 800 mA cm-2 current density. Cr0.4 Mo0.6 B2 has excellent long-term stability and durability showing no significant activity loss after 5000 cycles and 25 h of operation in acid. First-principles calculations have correctly reproduced the nonlinear dependence of the c lattice parameter and have shown that the mixed metal/B layers, such as (110), promote hydrogen evolution more efficiently for x = 0.6, supporting the experimental results.