Flexible silicon solar cells with high power-to-weight ratios.

Silicon solar cells are a mainstay of commercialized photovoltaics, and further improving the power conversion efficiency of large-area and flexible cells remains an important research objective 1,2 . Here we report a combined approach to improving the power conversion efficiency of silicon heterojunction solar cells, while at the same time rendering them flexible. We use low-damage continuous-plasma chemical vapour deposition to prevent epitaxy, self-restoring nanocrystalline sowing and vertical growth to develop doped contacts, and contact-free laser transfer printing to deposit low-shading grid lines. High-performance cells of various thicknesses (55-130 μm) are fabricated, with certified efficiencies of 26.06% (57 μm), 26.19% (74 μm), 26.50% (84 μm), 26.56% (106 μm) and 26.81% (125 μm). The wafer thinning not only lowers the weight and cost, but also facilitates the charge migration and separation. It is found that the 57-μm flexible and thin solar cell shows the highest power-to-weight ratio (1.9 W g -1 ) and open-circuit voltage (761 mV) compared to the thick ones. All of the solar cells characterized have an area of 274.4 cm 2 , and the cell components ensure reliability in potential-induced degradation and light-induced degradation ageing tests. This technological progress provides a practical basis for the commercialization of flexible, lightweight, low-cost and highly efficient solar cells, and the ability to bend or roll up crystalline silicon solar cells for travel is anticipated.