Redox Interaction between Selenite and Mackinawite in Cement Pore Water.

In cement-rich radioactive waste repositories, mackinawite (FeS) forms at the steel corrosion interface within reinforced concrete and potentially retards the transport of redox-sensitive radionuclides (e.g., 79 Se) in porous cement media. Redox interactions between selenite and mackinawite under hyperalkaline conditions remain unclear and require further investigations. Here, using comprehensive characterization on both aqueous and solid speciation, we successfully monitored the whole interaction process between selenite and mackinawite under hyperalkaline conditions. The results show similar chemical environments for SeO 3 2- and S 2- /S n 2- at the mackinawite-water interface, verifying an immediate reduction. After 192 h of reaction, SeO 3 2- was reduced to solid Se 0 and SeS 2 species, accompanied by the oxidation of S 2- /S n 2- to S 2 O 3 2- and Fe(II) to Fe(III) in mackinawite. Aqueous speciation results showed that ∼99% of aqueous selenium was present as Se 4 S nanoparticles due to the dissolution of Se from the solid. In parallel, ∼62% of S 2- /S n 2- was released into the solution, with mackinawite transforming into magnetite, Fe(OH) 3 and FeS 2 O 3 + complexed to Cl - or OH - species, and magnetite subsequently dispersed in the solution. This study provides valuable data about the retardation mechanisms of redox-sensitive radionuclides by soluble iron sulfides, which is critical to advance our understanding of reactive concrete barriers used in nuclear waste disposal systems.