Preparation of Quick-Dissolving Nanofiber Face Masks Based on Needleless Electrostatic Spinning.

As the global facial mask market continues to grow, consumers have put forward higher requirements for the functionality and ingredients of mask products. Ordinary facial masks mostly use ordinary non-woven fabrics as the mask base fabric and are used with essence. Preservatives are generally added. At the same time, they are susceptible to the influence of the external environment and are easily oxidized, causing the mask to deteriorate and cause skin allergic reactions. In addition, traditional facial masks have problems such as poor fit with the skin, poor breathability, insufficient absorption of nutrient solutions, and easy dripping. The high specific surface area and high porosity of a nanofiber mask prepared by electrospinning technology are beneficial to the skin's absorption of nutrients, and it has good fit with the skin and strong breathability. A unique advantage of this nanofiber mask is that it uses spray. After the mask is sprayed with water or essence, the water-soluble polymer within it can be quickly dissolved, saving a lot of time. Nanofiber facial mask products can effectively solve consumer pain points and are conducive to the high-end development of facial masks. Therefore, this article combines needleless electrospinning technology to develop a new solid-state, preservative-free, quick-dissolving nanofiber facial mask that can be prepared on a large scale. Based on needleless electrospinning technology, this article deeply explores the process parameters and their influencing mechanisms for preparing nanofiber, quick-dissolving facial masks to achieve the stable preparation of nanofiber facial masks with the best morphology; a comprehensive analysis of the structure and influence of nanofiber facial masks from micro and macro perspectives demonstrates their performance and allows evaluation of them. The experimental results show that the mask morphology is optimal under the process conditions of using a spinning liquid of 20% collagen peptide solution, a spinning voltage of 30 kV, a collection distance of 19 cm, and a liquid supply speed of 130 mL/h.