Low-Temperature Dielectric Response of Strontium Titanate Thin Films Manipulated by Zn Doping.

The voltage dependence of the dielectric permittivity ε ' and the low dielectric loss tan δ of incipient ferroelectrics have drawn vast attention to the use of these materials for the development of tuning elements in electronics and telecommunications. Here, we study the DC electric field dependence of low-temperature ε ' in ~320 nm thick sol-gel-derived SrTi 1-x Zn x O 3-δ thin films with x = 0.01 and 0.05, deposited on Pt/TiO 2 /SiO 2 /Si substrates. Incorporation of Zn onto Ti sites is found to decrease ε ' compared to undoped SrTiO 3 films, while increasing the relative tunability n r up to ~32.9% under a DC electric field of 125 kV/cm at low temperatures. The hysteresis-free variation in ε ' with electric field and tan δ values below 0.6% observed for SrTi 1-x Zn x O 3-δ film with x = 0.01 make this compound more attractive for tunable device applications.