Wormlike micellar solutions formed by an anionic surfactant and a cationic surfactant with two head groups.

Innovation in the molecular structure of surfactants is important for the preparation of soft materials with novel properties. In this study, we synthesized a cationic surfactant, N 1 , N 1 , N 1 , N 1 , N 3 , N 3 , N 3 -pentamethyl- N 3 -(3-stearamidopropyl)propane-1,3-diammonium bromide, hereafter referred to as C18-DQA. Unlike conventional cationic surfactants, C18-DQA contains two quaternary ammonium head groups and a long-saturated alkyl chain equal to a chain length of 21 carbon atoms. C18-DQA exhibits a low Krafft point of ∼0 °C and a water solubility >1000 mM at 25 °C. The critical micelle concentration (cmc) of C18-DQA was determined to be 0.59 mM using the Nile red method. C18-DQA was mixed with sodium laurate (SL) at different molar ratios to produce transparent solutions with excellent viscoelasticity over a wide concentration range. The 1 : 1.5 molar ratio C18-DQA/SL mixed solutions exhibited gel-like behavior for a total surfactant concentration of 2.88 wt% (75 mM). The solution with a total surfactant concentration of 300 mM (120 mM C18-DQA and 180 mM SL) achieved a maximum zero-shear viscosity ( η 0 ) of 4224 Pa s. Cryogenic transmission electron microscopy analysis revealed the formation of extremely long wormlike micelles, with a cross-sectional diameter of 5 nm and contour length >3 μm, in the mixed solutions. C18-DQA and SL molecules were drawn close by electrostatic attractions, leading to a suitable molecular geometry for the extensive growth of wormlike micelles. This work will act as an important reference for the future preparation of highly viscoelastic solutions by mixing cationic and anionic surfactants. The proposed system is also expected to have potential applications in cosmetic formulations, home care products, and oilfield fracturing fluids.