Increase of Solid Polymer Electrolyte Ionic Conductivity Using Nano-SiO2 Synthesized from Sugarcane Bagasse as Filler.

The synthesize of solid polymer electrolyte (SPE) based on polyethylene oxide (PEO), NaClO4 and nano-SiO2 was carried out by solution cast technique. Nano-SiO2 was synthesized from sugarcane bagasse using sol-gel method. FTIR analysis was carried out to investigate the bonding between nano-SiO2 and PEO/NaClO4. The morphology of the SPE was characterized using SEM. XRD and DSC analysis showed that SPE crystallinity decreased as nano-SiO2 concentration was increased. Mechanical analyses were conducted to characterize the SPE tensile strength and elongation at break. EIS analysis was conducted to measure SPE ionic conductivity. The PEO/NaClO4 SPE with the addition of 5% nano-SiO2 from sugarcane bagasse at 60 °C produced SPE with the highest ionic conductivity, 1.18 × 10-6 S/cm. It was concluded that the addition of nano-SiO2 increased ionic conductivity and interface stability at the solid polymer electrolyte-PEO/NaClO4.