Large Improvement of Thermoelectric Performance by Magnetism in Co-Based Full-Heusler Alloys.
Zhigang GuiGuiwen WangHonghui WangYuqing ZhangYanjun LiXikai WenYikang LiKunling PengXiaoyuan ZhouJianjun YingXianhui ChenPublished in: Advanced science (Weinheim, Baden-Wurttemberg, Germany) (2023)
Full-Heusler alloys (fHAs) exhibit high mechanical strength with earth-abundant elements, but their metallic properties tend to display small electron diffusion thermopower, limiting potential applications as excellent thermoelectric (TE) materials. Here, it is demonstrated that the Co-based fHAs Co 2 XAl (X = Ti, V, Nb) exhibit relatively high thermoelectric performance due to spin and charge coupling. Thermopower contributions from different magnetic mechanisms, including spin fluctuation and magnon drag are extracted. A significant contribution to thermopower from magnetism compared to that from electron diffusion is demonstrated. In Co 2 TiAl, the contribution to thermopower from spin fluctuation is higher than that from electron diffusion, resulting in an increment of 280 µW m -1 K -2 in the power factor value. Interestingly, the thermopower contribution from magnon drag can reach up to -47 µV K -1 , which is over 2400% larger than the electron diffusion thermopower. The power factor of Co 2 TiAl can reach 4000 µW m -1 K -2 which is comparable to that of conventional semiconducting TE materials. Moreover, the corresponding figure of merit zT can reach ≈0.1 at room temperature, which is significantly larger than that of traditional metallic materials. The work shows a promising unconventional way to create and optimize TE materials by introducing magnetism.