Atomic Layer Deposited TiO₂ and Al₂O₃ Thin Films as Coatings for Aluminum Food Packaging Application.

Vanessa DiasHomero MacielMariana Amorim FragaAnderson O LoboRodrigo PessoaFernanda Roberta Marciano
Published in: Materials (Basel, Switzerland) (2019)
Titanium dioxide (TiO₂) and aluminum oxide (Al₂O₃) coatings have been investigated in a wide range of bio-applications due to their biodegradation and biocompatibility properties, that are key parameters for their use in the food packaging and biomedical devices fields. The present study evaluates and compares the electrochemical behavior of the non-coated, commercial resin-coated, TiO₂-coated and Al₂O₃-coated aluminum in commercial beer electrolyte. For this, TiO₂ and Al₂O₃ thin films were deposited on aluminum (Al) substrates using atomic layer deposition (ALD). The evaluation of the corrosion barrier layer properties was performed by linear sweep voltammetry (LSV) during 10 min and electrochemical impedance spectroscopy (EIS). In addition, profilometry, grazing incidence X-ray diffractometry (GIXRD), scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR) analyses were performed to investigate the physical and chemical properties of the pristine and / or corroded samples. TiO₂ and Al₂O₃ films presented an amorphous structure, a morphology that follows Al substrate surface, and a thickness of around 100 nm. Analysis of LSV data showed that ALD coatings promoted a considerable increase in corrosion barrier efficiency being 86.3% for TiO₂-coated Al and 80% for Al₂O₃-coated Al in comparison with 7.1% of commercial resin-coated Al. This is mainly due to the lower electrochemical porosity, 11.4% for TiO₂-coated Al and 20.4% for Al₂O₃-coated Al in comparison with 96% of the resin-coated Al, i.e. an increase of up to twofold in the protection of Al when coated with TiO₂ compared to Al₂O₃. The EIS results allow us to complement the discussions about the reduced corrosion barrier efficiency of the Al₂O₃ film for beer electrolyte once SEM and FT-IR analyzes did not show drastic changes in both investigated ALD films after the corrosion assays. The above results indicate that ALD TiO₂ and Al₂O₃ films may be a viable alternative to replace the synthetic resin coatings frequently used in aluminum cans of use in the food industry.
Keyphrases