Energy transfer properties of a single-phase Na 3 Gd(PO 4 ) 2 :Eu 2+ ,Mn 2+ phosphor with excellent thermal stability for w-LEDs.

A high temperature solid state method was used to prepare Na 3 Gd(PO 4 ) 2 :Eu 2+ ,Mn 2+ phosphors with good thermal stability. The phosphor shows a broadband excitation region of 250-430 nm, which can be matched with the emissions of ultraviolet (UV)/near-ultraviolet (NUV) LED chips for white light emitting diodes (w-LEDs). The energy transfer efficiency is 74.46% from the sensitizer Eu 2+ ions to the activator Mn 2+ ions, which enhances the intensities of the Na 3 Gd(PO 4 ) 2 -based phosphor. In addition, by increasing the Mn 2+ doping level in the phosphor, the Na 3 Gd(PO 4 ) 2 :Eu 2+ ,Mn 2+ phosphor first shows blue light, then turns to white light, and finally emits red light under 365 nm excitation. Besides, the temperature-dependent photoluminescence measurements indicate that the prepared phosphors exhibit good thermal stability. W-LEDs fabricated by combining a 365 nm chip with the Na 3 Gd(PO 4 ) 2 :Eu 2+ ,Mn 2+ phosphor exhibit bright white light, which has a high color rendering index (CRI) = 91.5, and a relatively low correlated color temperature (CCT) = 5198 K. Moreover, the CIE point is calculated to be at (0.3337, 0.3465), which is located in the white light region. These results indicate that the as-prepared phosphors can be considered as potential candidates for UV/NUV light-excited w-LED applications.