Intermediate-Temperature Tensile Behavior of a Hot-Rolled Mg-Li-Al-Cd-Zn Alloy.

Developing light structure materials that work stably at elevated temperatures is a long-standing challenge for many application fields, particularly in the development of aerospace equipment. Zn/Cd alloying elements were prospected to improve the stability of the lightest Mg-Li based alloys; however, little is known about the intermediate-temperature mechanical properties of such alloys. The present work investigated the tensile behaviors of a cold-rolled Mg-Li-Al-Cd-Zn alloy in a temperature range of 30-150 °C. The results indicate that the alloy can host a tensile strength σ UTS of 108~121 MPa, a yield strength σ YP of 97~109 MPa and elongation ε B of 14-15 % at 150 °C, dependent on the tensile direction. The mechanical properties intensively are modulated by temperature through the competition between work hardening and softening. Work hardening due to dislocation blocking by the precipitated MgLi 2 X phase dominated the deformation at low temperatures, while softening that resulted from dynamic recrystallization was the main effect at high temperatures. Correspondingly, a quasi-cleavage mechanism dominated the fracture at temperatures near room temperature, and microvoid coalescence worked at high temperatures above 100 °C. Our results offer a new experimental understanding of the elevated-temperature mechanical behaviors of Mg-Li alloys and will advance the development of new light magnesium alloys with high stability.