Mangiferin-Enriched Mn-Hydroxyapatite Coupled with β-TCP Scaffolds Simultaneously Exhibit Osteogenicity and Anti-Bacterial Efficacy.

Biphasic calcium phosphate (BCP) containing β-tricalcium phosphate and manganese (Mn)-substituted hydroxyapatite (HAP) was synthesized. Biomedical scaffolds were prepared using this synthesized powder on a sacrificial polyurethane sponge template after the incorporation of mangiferin (MAN). Mn was substituted at a concentration of 5% and 10% in HAP to examine the efficacy of Mn at various concentrations. The phase analysis of the as-formed BCP scaffold was carried out by X-ray diffraction analysis, while the qualitative observation of morphology and the osteoblast cell differentiation were carried out by scanning electron microscopy and confocal laser scanning microscopy techniques. Gene expressions of osteocalcin, collagen 1, and RUNX2 were carried out using qRT-PCR analyses. Significantly higher ( p < 0.05) levels of ALP activity were observed with extended osteoblast induction on the mangiferin-incorporated BCP scaffolds. After characterization of the specimens, it was found that the scaffolds with 10% Mn-incorporated BCP with mangiferin showed better osteogenicity and simultaneously the same scaffolds exhibited higher anti-bacterial properties as observed from the bacterial viability test. This study was carried out to evaluate the efficacy of Mn and MAN in BCP for osteogenicity and antibacterial action.