Surprisingly Low Reactivity of Layered Manganese Oxide toward Water Oxidation in Fe/Ni-Free Electrolyte under Alkaline Conditions.

So far, many studies on the oxygen-evolution reaction (OER) by Mn oxides have been focused on activity; however, the identification of the best performing active site and corresponding catalytic cycles is also of critical importance. Herein, the real intrinsic activity of layered Mn oxide toward OER in Fe/Ni-free KOH is studied for the first time. At pH ≈ 14, the onset of OER for layered Mn oxide in the presence of Fe/Ni-free KOH happens at 1.72 V (vs reversible hydrogen electrode (RHE)). In the presence of Fe ions, a 190 mV decrease in the overpotential of OER was recorded for layered Mn oxide as well as a significant decrease (from 172.8 to 49 mV/decade) in the Tafel slope. Furthermore, we find that both Ni and Fe ions increase OER remarkably in the presence of layered Mn oxide, but that pure layered Mn oxide is not an efficient catalyst for OER without Ni and Fe under alkaline conditions. Thus, pure layered Mn oxide and electrolytes are critical factors in finding the real intrinsic activity of layered Mn oxide for OER. Our results call into question the high efficiency of layered Mn oxides toward OER under alkaline conditions and also elucidate the significant role of Ni and Fe impurities in the electrolyte in the presence of layered Mn oxide toward OER under alkaline conditions. Overall, a computational model supports the conclusions from the experimental structural and electrochemical characterizations. In particular, substitutional doping with Fe decreases the thermodynamic OER overpotential up to 310 mV. Besides, the thermodynamic OER onset potential calculated for the Fe-free structures is higher than 1.7 V (vs RHE) and, thus, not in the stability range of Mn oxides.