Degradation at the Na 3 SbS 4 /Anode Interface in an Operating All-Solid-State Sodium Battery.

All-solid-state sodium batteries utilize earth-abundant elements and are sustainable systems for large-scale energy storage and electric transportation. Replacing flammable carbonate-based electrolytes with solid-state ionic conductors promotes battery safety. Using solid-state electrolytes (SEs) also eliminates the need for packing when fabricating tandem cells, potentially enabling further enhanced energy density. Na 3 SbS 4 , a Na + conductor, remains stable in dry air and shows high Na + conductivity (σ ≈ 1.0 × 10 -3 S/cm) and is thus a promising SE for applications in sodium batteries. However, upon repeated electrochemical cycling, Na 3 SbS 4 -containing Na batteries exhibit decaying capacity and limited cycle life, which is likely associated with the decomposition of Na 3 SbS 4 at the electrode/electrolyte interface. This work presents an in-depth analysis of the decomposition chemistry occurring at the Na 3 SbS 4 /anode interface using combined in situ Raman and post-mortem characterization. The results indicate that the SbS 4 3- counterion is electrochemically reduced when experiencing Na + reduction potentials, and this reduction chemistry likely follows multiple pathways. The observed reduction products include SbS 3 3- , the Sb 2 S 7 4- dimer, the NaSb binary phase, and Na 2 S. We also observed the irreversibility of the decomposition and, as a consequence, the accumulation of the degradation products over cycles. Also notable is the heterogeneity of this degradation chemistry across the interface. Through the spectroelectrochemical characterizations, we reveal the possible mechanisms of the Na 3 SbS 4 decomposition at the solid electrolyte/anode interface in an operating device.