Crosslinking Vinyl-Addition Polynorbornenes via Difunctional Diazirines to Generate Low Dielectric-Constant and Low Dielectric-Loss Thermosets.

Pramod KandanarachchiGerhard A MeyerStefania F MusolinoJeremy E WulffLarry F Rhodes
Published in: Macromolecular rapid communications (2024)
Thermosets having low dielectric constant (Dk < 3) and low dielectric dissipation factor (Df < 0.003), high glass transition temperature (Tg > 150 °C), and good adhesion to copper are desirable for the low loss layers of the copper clad laminates (CCL) in next generation printed circuit boards (PCB). Three different difunctional diazirines were evaluated for both thermal and photochemical crosslinking of a high Tg vinyl-addition polynorbornene resin: poly(5-hexyl-1-norbornene) (poly(HNB)). The substrate polymer, crosslinked by the carbenes generated from the activated diazirines, formed thermosets with Dk < 2.3 and Df < 0.001 at 10 GHz depending on the identity of the diazirine and the loading. The Dk and Df values for one composition were stable for 1600 h at 125 °C in air and for 1400 h at 85 °C and 85% relative humidity, suggesting good long-term reliability of this thermoset. Adhesion of poly(HNB) to copper can be enhanced by priming the copper surface with a diazirine prior to high temperature lamination; peel strength values of greater than 7.5 N/cm were achieved. Negative-tone photopatterning of poly(HNB) with diazirines upon exposure to 365 nm light was demonstrated. This article is protected by copyright. All rights reserved.
Keyphrases
  • high temperature
  • escherichia coli
  • pseudomonas aeruginosa
  • staphylococcus aureus
  • hyaluronic acid
  • drug induced