Manipulating the thermometric behaviors of Er 3+ /Yb 3+ /Ho 3+ -tridoped La 2 Mo 3 O 12 polychromatic upconverting microparticles via adjusting spatial mode and a sensing strategy.
Huocheng LvXiaoqing LaiWeiping LiLaihui LuoPeng DuPublished in: Physical chemistry chemical physics : PCCP (2023)
To meet the needs of contactless optical thermometry, Er 3+ /Yb 3+ /Ho 3+ -tridoped La 2 Mo 3 O 12 (LMO) microparticles were designed and synthesized. Upon exciting with 980 nm light, the synthesized compounds emit glaring upconversion (UC) emissions and their emission colors can be tuned from green to yellow by altering the Ho 3+ content. It is found that the optimal doping contents for Yb 3+ and Ho 3+ in LMO are 9 and 1 mol%, respectively, and the UC emission mechanism involved is a two-photon harvest process. Using the fluorescence intensity ratio (FIR) technique to analyze the temperature responses of the UC emissions arising from thermally coupled levels (TCLs) and non-thermally coupled levels (non-TCLs), the temperature sensing abilities of the synthesized samples were investigated. When the TCLs of Er 3+ ( 2 H 11/2 , 4 S 3/2 ) are used, the synthesized microparticles present the highest absolute and relative sensitivities of 0.0085 and 1.0236% K -1 , respectively. Moreover, when the non-TCLs of Er 3+ ( 2 H 11/2 ) and Ho 3+ ( 5 F 5 ) are used, the maximum absolute and relative sensitivities of the synthesized compounds are 0.0296 and 0.6287% K -1 , respectively. Clearly, the thermometric characteristics of the final products can be regulated via using different sensing strategies ( i.e. , TCLs and non-TCLs) and emission combinations ( i.e. , spatial mode). However, the change of the Ho 3+ content has little impact on the temperature sensing capacity of the synthesized products. These results indicate that Er 3+ /Yb 3+ /Ho 3+ -tridoped LMO microparticles are promising candidates for optical thermometers and our findings also provide possible strategies for regulating the thermometric properties of rare-earth ion doped luminescent materials.