Effects of Power and Laser Speed on the Mechanical Properties of AlSi7Mg0.6 Manufactured by Laser Powder Bed Fusion.

The AlSi7Mg0.6 alloy, with its good tolerance against strain, is used in laser powder bed fusion (LPBF) to produce parts with complex geometries for aerospace engineering. Production of parts with good mechanical strength requires, however, the optimization of laser parameters. This study thus evaluated the influence of scanning speed, laser power, and strategy on several mechanical properties (tensile/resilience/hardness) to identify an optimal processing region. Results have shown the profound influence of laser power and scanning speed on mechanical properties, with a limited influence from the laser strategy. Tensile strength values ranging from 122 to 394 MPa were obtained, while Young's Modulus varied from 17 to 29 GPa, and the elongation at break ranged from 2.1 to 9.8%. Surface plots of each property against laser power and speed revealed a region of higher mechanical properties. This region is found when using 50 µm thick layers for energy densities between 25 and 35 J/mm 3 . Operating at higher values of energy density yielded sub-optimal properties, while a lower energy density resulted in poor performances. Results have shown that any optimization strategy must not only account for the volumic energy density value, but also for laser power itself when thick layers are used for fabrication. This was shown through parts exhibiting reduced mechanical performances that were produced within the optimal energy density range, but at low laser power. By combining mid-speed and power within the optimal region, parts with good microstructure and limited defects such as balling, keyhole pores, and hot cracking will be produced. Heat-treating AlSi7Mg0.6 parts to T6 temper negatively affected mechanical performances. Adapted tempering conditions are thus required if improvements are sought through tempering.