Induced Anionic Functional Group Orientation-Assisted Stable Electrode-Electrolyte Interphases for Highly Reversible Zinc Anodes.

Dendrite growth and other side-reaction problems of zinc anodes in aqueous zinc-ion batteries heavily affect their cycling lifespan and Coulombic efficiency, which can be effectively alleviated by the application of polymer-based functional protection layer on the anode. However, the utilization rate of functional groups is difficult to improve without destroying the polymer chain. Here, a simple and well-established strategy is proposed by controlling the orientation of functional groups (─SO 3 H) to assist the optimization of zinc anodes. Depending on the electrostatic effect, the surface-enriched ─SO 3 H groups increase the ionic conductivity and homogenize the Zn 2+ flux while inhibiting anionic permeation. This approach avoids the destruction of the polymer backbone by over-sulfonation and amplifies the effect of functional groups. Therefore, the modified sulfonated polyether ether ketone (H-SPEEK) coating-optimized zinc anode is capable of longtime stable zinc plating/stripping, and moreover an enhanced cycling steadiness under high current densities is also detected in a series of Zn batteries with different cathode materials, which achieved by the inclusion of H-SPEEK coating without causing any harmful effects on the electrolyte and cathode. This work provides an easy and efficient approach to further optimize the plating/stripping of cations on metal electrodes, and sheds lights on the scale-up of high-performance aqueous zinc-ion battery technology.