Effects of Co-Solvent-Induced Self-Assembled Graphene-PVDF Composite Film on Piezoelectric Application.

Januar WidakdoWen-Ching LeiAnawati AnawatiSubrahmanya Thagare ManjunathaHannah Faye M AustriaOwen SetiawanTsung-Han HuangYu-Hsuan ChiaoWei-Song HungMing-Hua Ho
Published in: Polymers (2022)
A persistent purpose for self-powered and wearable electronic devices is the fabrication of graphene-PVDF piezoelectric nanogenerators with various co-solvents that could provide enhanced levels of durability and stability while generating a higher output. This study resulted in a piezoelectric nanogenerator based on a composite film composed of graphene, and poly (vinylidene fluoride) (PVDF) as a flexible polymer matrix that delivers high performance, flexibility, and cost-effectiveness. By adjusting the co-solvent in the solution, a graphene-PVDF piezoelectric nanogenerator can be created (acetone, THF, water, and EtOH). The solution becomes less viscous and is more diluted the more significant the concentration of co-solvents, such as acetone, THF, and EtOH. Additionally, when the density is low, the thickness will be thinner. The final film thickness for all is ~25 µm. Furthermore, the- crystal phase becomes more apparent when graphene is added and combined with the four co-solvents. Based on the XRD results, the peak changes to the right, which can be inferred to be more dominant with the β-phase. THF is the co-solvent with the highest piezoelectric output among other co-solvents. Most of the output voltages produced are 0.071 V and are more significant than the rest.
Keyphrases