Highly Zeolite-Loaded Polyvinyl Alcohol Composite Membranes for Alkaline Fuel-Cell Electrolytes.

Po-Ya HsuTing-Yu HuSelvaraj Rajesh KumarChia-Hao ChangKevin C-W WuKuo-Lun TungShingjiang Jessie Lue
Published in: Polymers (2018)
Having a secure and stable energy supply is a top priority for the global community. Fuel-cell technology is recognized as a promising electrical energy generation system for the twenty-first century. Polyvinyl alcohol/zeolitic imidazolate framework-8 (PVA/ZIF-8) composite membranes were successfully prepared in this work from direct ZIF-8 suspension solution (0⁻45.4 wt %) and PVA mixing to prevent filler aggregation for direct methanol alkaline fuel cells (DMAFCs). The ZIF-8 fillers were chosen for the appropriate cavity size as a screening aid to allow water and suppress methanol transport. Increased ionic conductivities and suppressed methanol permeabilities were achieved for the PVA/40.5% ZIF-8 composites, compared to other samples. A high power density of 173.2 mW cm-2 was achieved using a KOH-doped PVA/40.5% ZIF-8 membrane in a DMAFC at 60 °C with 1⁻2 mg cm-2 catalyst loads. As the filler content was raised beyond 45.4 wt %, adverse effects resulted and the DMAFC performance (144.9 mW cm-2) was not improved further. Therefore, the optimal ZIF-8 content was approximately 40.5 wt % in the polymeric matrix. The specific power output was higher (58 mW mg-1) than most membranes reported in the literature (3⁻18 mW mg-1).
Keyphrases