Nickel Chalcogenide Nanoparticles-Assisted Photothermal Solar Driven Membrane Distillation (PSDMD).

Developing photothermal solar driven membrane distillation (PSDMD) is of great importance in providing fresh water for remote off-grid regions. The production of freshwater through the PSDMD is driven by the temperature difference between feed and distillate sides created via the addition of efficient photothermal nanostructures. Here we proposed nickel sulfides and nickel tellurium nanoparticles (NPs) to be loaded into the polymeric membrane to enhance its performance. Ag and CuSe NPs are also considered for comparison as they are previously used for membrane distillation (MD). Our theoretical approach showed that all of the considered NPs increased the temperature of the PVDF membrane by around a few degrees. NiS and NiTe2 NPs are the most efficient solar light-to-heat converters compared to NiTe and NiS2 NPs due to their efficient absorption over the visible range. PVDF membrane loaded with 25% of NiCs NPs and a porosity of 32% produced a transmembrane vapor flux between 22 and 27 L/m 2 h under a 10-times-amplified sun intensity. Under the same conditions, the PVDF membrane loaded with CuSe and Ag NPs produced 15 and 18 L/m 2 h of vapor flux, respectively. The implantation of NPs through the membrane not only increased its surface temperature but also possessed a high porosity which provided a higher distillation and energy efficiency that reached 58% with NiS NPs. Finally, great agreement between our theoretical model and experimental measurement is obtained.