Flux-assisted synthesis of tungsten-doped layered perovskite oxychloride with promoted visible-light-responsive O 2 evolution performance.

Here, we successfully prepared Ba 2 Bi 3 Ta 2 O 11 Cl via a simple one-step molten salt method and adjusted its crystal morphology and structure, based on which the O 2 -evolving activity was significantly improved. In addition, W doping promotes the charge separation efficiency, lowers the energy barrier for water oxidation reaction, and thus improves the activity. Finally, the optimized W-doped sample after molten salt treatment shows the best O 2 production activity (55 μmol h -1 ) without loading any cocatalyst, which is 6 times higher than that of pristine Ba 2 Bi 3 Ta 2 O 11 Cl and 2 times higher than that of the undoped Ba 2 Bi 3 Ta 2 O 11 Cl treated with molten salt, respectively.