The Impact of β-Radiation Crosslinking on Flammability Properties of PA6 Modified by Commercially Available Flame-Retardant Additives.
Florian TomiakDietmar DrummerPublished in: Polymers (2022)
A comparative study was conducted investigating the influence of β-radiation crosslinking (β-RC) on the fire behavior of flame retardant-modified polyamide 6 (PA6). In order to provide a comprehensive overview, a variety of commercially available flame-retardant additives were investigated, exhibiting different flame retarding actions such as delusion, char formation, intumescence and flame poisoning. This study focused on the identification of differences in the influence of β-RC on fire behavior. Coupled thermal gravimetrical analysis (TGA) and Fourier transformation infrared spectroscopy (FTIR) were used to conduct changes within the decomposition processes. Dynamic thermal analysis (DTA) was used to identify structural stability limits and fire testing was conducted using the limiting oxygen index (LOI), vertical UL-94 and cone calorimeter testing. Crosslinking was found to substantially change the fire behavior observed, whereas the observed phenomena were exclusively physical for the given formulations studied: warpage, char residue destruction and anti-dripping. Despite these phenomena being observed for all β-RC formulations, the impact on fire resistivity properties were found to be very different. However, the overall fire protection properties measured in UL-94 fire tests were found to deteriorate for β-RC formulations. Only β-RC formulations based on PA6/EG were found to achieve a UL-94 V0 classification.