Formulation and Characterization of New Experimental Dental Composites with Zirconium Filling in Different Forms.

Dipa Rani MohajonDoina ProdanMărioara MoldovanIoan PeteanMariana PacurarMiuta Rafila FilipRahela CarpaGeorgiana Florentina GheorgheCodruţa Liana Saroşi
Published in: Materials (Basel, Switzerland) (2024)
Short glass fibers are generally used in posterior dental restorations to enhance the mechanical properties and improve the material microstructure. Two resin-based composites (S0 and SF) were formulated and characterized to investigate the influence of zirconium in their characteristics and properties. The organic part of the investigated materials was the same (BisGMA, TEGDMA, and a photochemical polymerization system), and in the inorganic part, besides quart, glassA, and hydroxylapatite with Zn, sample S0 contained strontium glass with zirconium and sample SF contained fiber powder of chopped zirconium. The samples were characterized by the degree of conversion (DC), mechanical properties, water sorption (WS), scanning electron microscopy (SEM), atomic force microscopy (AFM) before and after the WS test, and antimicrobial properties. The results obtained were subjected to one-way ANOVA and Tukey's statistical tests. Both samples had a high DC. Regarding the mechanical properties, both samples were very similar, except DTS, which was higher for the composite without fibers. After 14 days, the WS value of the SF sample was lower than that of the S0 sample. Water caused significant changes in the topography of the SF sample, but thanks to its antimicrobial properties and the diffusion phenomenon, SF had a more pronounced antimicrobial effect. This study shows that the addition of appropriate amounts of Sr-Zr-glass powder gives the material in which it is added similar properties to material containing chopped zirconium glass fiber powder. According to the antimicrobial test results, resin composites containing experimental zirconia fillings can be considered in future in vitro clinical studies for posterior reconstructions with significantly improved mechanical properties.
Keyphrases