Crystallization Behavior of the Low-Temperature Mineralization Sintering Process for Glass Nanoparticles.
Yeongjun SeoTomoyo GotoSung Hun ChoTohru SekinoPublished in: Materials (Basel, Switzerland) (2020)
Bioactive glasses are promising materials for various applications, such as bone grafts and implants. The development of sintering techniques for bioactive glasses is one of the most important ways to expand the application to biomaterials. In this paper, we demonstrate the low-temperature mineralization sintering process (LMSP) of glass nanoparticles and their crystallization behavior. LMSP is a novel process employed to densify glass nanoparticles at an extremely low temperature of 120 °C. For this new approach, the hydrothermal condition, mineralization, and the nanosize effect are integrated into LMSP. To induce mineralization in LMSP, bioactive glass nanoparticles (BGNPs, 55SiO2-40CaO-5P2O5, mol%), prepared by the sol-gel process, were mixed with a small amount of simulated body fluid (SBF) solution. As a result, 93% dense BGNPs were realized under a temperature of 120 °C and a uniaxial pressure of 300 MPa. Due to the effect of mineralization, crystalline hydroxyapatite (HAp) was clearly formed at the boundaries of BGNPs, filling particles and interstitials. As a result, the relative density was remarkably close to that of the BGNPs conventionally sintered at 1050 °C. Additionally, the Vickers hardness value of LMSP samples varied from 2.10 ± 0.12 GPa to 4.28 ± 0.11 GPa, and was higher than that of the BGNPs conventionally sintered at 850 °C (2.02 ± 0.11 GPa). These results suggest that, in addition to LMSP being an efficient densification method for obtaining bulk bioactive glasses at a significantly lower temperature level, this process has great potential for tissue engineering applications, such as scaffolds and implants.