Magnetic and Magneto-Optical Oroperties of Iron Oxides Nanoparticles Synthesized under Atmospheric Pressure.

Magnetite nanoparticles were synthesized by a simple thermal decomposition process, involving only iron (III) nitrate nonahydrate as a precursor, and hexadecylamine as a solvent and stabilizer at reaction temperatures varied from 200 to 380 °C. The results of the structural analysis showed that the average crystallite size depends on the reaction temperature and increases from 4.8 to 13.3 nm. The behavior of the coercivity indicates that all synthesized samples are single domain; herewith, it was found that the critical size corresponding to the transition to the superparamagnetic state at room temperature is about 9 nm. The effect of the reaction temperature on changes in the saturation magnetization was studied. It was found that the size effect in the MCD spectra is observed for the IVCT transition and one ISCT transition, and the influence of the reaction temperature on the change in the MCD spectra was discussed.