Evaluation of flame retardancy and flexural property on prepared plastic disks containing known concentrations of flame retardants through simulated weathering tests.

The standardized acrylonitrile-butadiene-styrene (ABS) or polycarbonate (PC) resin disk with added flame retardants (FRs) has a potential to be a suitable tool for predictions of both aging of the plastic materials and release rate of a flame retardants exposed under different outdoor and indoor conditions. The experiments examined the dynamics and kinetics of the release of dechlorane plus, tetrabromobisphenol A, triphenyl phosphate and antimony trioxide as FRs from a standardized plastic disk before and after exposure to artificial sunlight. Assessments were carried out independently to measure changes in the content of flame retardants and monitor the flame retardancy and flexural properties after exposure (60 W/m2) over a period of 200 h and 500 h, which are reasonable to predict a short-time tendency and to receive any advice for a safe re-use. The releases of three organic flame retardants and four elements (Cl, Br, P and Sb) from weathered ABS and PC disks were very limited, except for surface delamination and resin microparticles. Triphenyl phosphate was stable without hydrolysis, while the degradation of tetrabromobisphenol A was observed (approximately 20% decrease for ABS disk and approximately 50% decrease for PC disk). During the study, no significant differences in the flame retardancy and flexural properties of the disks could be detected. In practice, the results obtained from disks of acrylonitrile-butadiene-styrene or polycarbonate resin with selected flame retardants used in specific conditions may provide technical expertise regarding weathering processes.