Room Temperature Crystallized Phase-Pure α-FAPbI 3 Perovskite with In-Situ Grain-Boundary Passivation.

Energy loss in perovskite grain boundaries (GBs) is a primary limitation toward high-efficiency perovskite solar cells (PSCs). Two critical strategies to address this issue are high-quality crystallization and passivation of GBs. However, the established methods are generally carried out discretely due to the complicated mechanisms of grain growth and defect formation. In this study, a combined method is proposed by introducing 3,4,5-Trifluoroaniline iodide (TFAI) into the perovskite precursor. The TFAI triggers the union of nano-sized colloids into microclusters and facilitates the complete phase transition of α-FAPbI 3 at room temperature. The controlled chemical reactivity and strong steric hindrance effect enable the fixed location of TFAI and suppress defects at GBs. This combination of well-crystallized perovskite grains and effectively passivated GBs leads to an improvement in the open circuit voltage (V oc ) of PSCs from 1.08 V to 1.17 V, which is one of the highest recorded V oc without interface modification. The TFAI-incorporated device achieved a champion PCE of 24.81%. The device maintained a steady power output near its maximum power output point, showing almost no decay over 280 h testing without pre-processing.