1000 °C High-Temperature Wetting Behaviors of Molten Metals on Laser-Microstructured Metal Surfaces.
Xinyu HuGuochen JiangPeixun FanGuoqiang HuGang XuWei WangLizhong WangHongjun ZhangMinlin ZhongPublished in: Langmuir : the ACS journal of surfaces and colloids (2023)
The melting of metals at high temperatures is common and important in many fields, e.g., metallurgy, refining, casting, welding, brazing, even newly developed batteries, and nuclear fusion, which is thus of great value in modern industrialization. However, the knowledge of the wetting behaviors of molten metals on various substrate surfaces remains insufficient, especially when the temperature is over 1000 °C and with microstructured metal substrate surfaces. Herein, we selected molten cerium (Ce) on a tantalum (Ta) substrate as an example and investigated in detail its wetting at temperatures up to 1000 °C by modulating the microstructures of the substrate surfaces via laser processing. We discovered that the wetting states of molten Ce on Ta surfaces at temperatures over 900 °C could be completely altered by modifying the laser-induced surface microstructures and the surface compositions. The molten Ce turned superlyophilic with its contact angle (CA) below 10° on the only laser-microstructured surfaces, while it exhibited lyophobicity with a CA of about 135° on the laser-microstructured plus oxidized ones, which demonstrated remarkably enhanced resistance against the melt with only tiny adhesion in this circumstance. In contrast, the CA of molten Ce on Ta substrate surfaces only changed from ∼25 to ∼95° after oxidization without laser microstructuring. We proved that modulating the substrate surface microstructures via laser together with oxidization was capable of efficiently controlling various molten metals' wetting behaviors even at very high temperatures. These findings not only enrich the understanding of molten metal high-temperature wettability but also enable a novel practical approach to control the wetting states for relevant applications.