High-performance n-type organic thermoelectrics enabled by modulating cyano-functionalized polythiophene backbones.

The scarcity of n-type polymers with high electrical conductivity ( σ ) and power factor (PF) is the major challenge for organic thermoelectrics (OTEs). By integrating cyano functionalities and an intramolecular conformation lock, we herein synthesize a new electron-deficient building block, CNg4T2, bearing long 1,4,7,10-tetraoxahendecyl side chains, and then further develop two n-type polythiophene derivatives, CNg4T2-2FT and CNg4T2-CNT2, with 3,4-difluorothiophene and 3,3'-dicyano-2,2'-bithiophene as co-units, respectively. Compared with CNg4T2-2FT, CNg4T2-CNT2 features a deeper-positioned lowest unoccupied molecular orbital (LUMO) while maintaining a high degree of backbone coplanarity. As a consequence, the CNg4T2-CNT2 film with molecular dopant N-DMBI delivered an impressive σ of 13.2 S cm -1 and a high PF of up to 10.84 μW m -1 K -2 , significantly outperforming CNg4T2-2FT and benchmark n-type polymer N2200 films. To the best of our knowledge, this PF of CNg4T2-CNT2 devices is the highest value for n-type polythiophenes in OTEs. Further characterizations indicate that the high performance of CNg4T2-CNT2-based devices is attributed to the high doping efficiency and ordered packing of polymer chains. Our study demonstrates that CNg4T2 is a highly appealing electron-deficient building block for n-type OTE polymers and also suggests that fine-tuning of the polymer backbone is a powerful approach to accessing high-performance n-type polymers for OTE devices.