Microstructural Aspects of the Fabrication of Al/Al 2 O 3 Composite by Friction Stir Processing.

The purpose of this work was the examination of microstructural evolution during the fabrication of an Al/Al 2 O 3 composite by friction stir processing (FSP). In order to obtain new insight into this process, a longitudinal section of the produced composite was studied, and advanced characterization techniques (including electron backscatter diffraction and microhardness mapping) were applied. It was found that the reinforcing particles rapidly rearranged into the "onion-ring" structure, which was very stable against the subsequent dispersion. Specifically, the remnants of the comparatively coarse-scale particle agglomerations have survived even after 12 FSP passes. Therefore, it was concluded that three or four FSP passes, which are often applied in practice, are not sufficient to provide a homogeneous dispersion of the reinforcing particles. It was also revealed that the gradual distribution of the nanoscale Al 2 O 3 particles throughout the aluminum matrix promoted a subtle reduction in both the portion of high-angle boundaries and the average grain size. These observations were attributed to the particle pinning of grain-boundary migration and dislocation slip.