Temperature Dependence of the Electrical Properties of Na 2 Ti 3 O 7 /Na 2 Ti 6 O 13 /POMA Composites.

The temperature dependence of the electrical properties of composites formed by biphasic sodium titanate and poly( o -methoxyaniline) (Na 2 Ti 3 O 7 /Na 2 Ti 6 O 13 /POMA) with different concentrations of POMA (0%, 1%, 10%, 15%, 35% and 50%) in the ceramic matrix was determined from measurements of complex impedance. The structural details were studied by means of X-ray diffraction, confirming the formation of the Na 2 Ti 3 O 7 /Na 2 Ti 6 O 13 /POMA composites. The displacement of the (200) reflection from 2θ = 10.45° to 11.15° in the composites with 10 and 15% of POMA suggested the partial replacement of H + for Na + in the Na 2 Ti 3 O 7 structure. The thermal properties were investigated by Thermogravimetry and Differential Thermal Analysis. The Thermogravimetry curves of the composites with POMA content of 1, 10 and 15% presented profiles similar to that of pure sodium titanate sample. The composites with 35 and 50% of POMA showed a process at temperatures around 60-70 °C, which was associated with water absorbed by the polymer. The analysis of the complex impedance spectroscopy measurements revealed that the electrical resistivity of the composites in the range from 0 to 35% increased by two orders of magnitude, with different values for each concentration. This positive temperature coefficient of resistivity was less noticeable in the composite with highest POMA mass content (50%). The rapid increase in resistivity caused an increase in the relaxation time calculated from the time domain. The electrical response of the 50% of POMA compound changes in relation to what was observed in the other compounds, which suggests that there is a saturation limit in the increase in resistivity with POMA content.