Assessing Activation Quality through Evaporative Drying Patterns of Zr-MOF (UiO-66) Colloidal Droplets.

We demonstrate a simple droplet diagnostic approach to monitor the UiO-66 MOF (metal-organic framework) synthesis and its quality using the sessile droplet drying phenomenon. Drying a sessile droplet involves evaporation-driven hydrodynamic flow and particle-nature-dependent self-assembled deposition. In general, the MOF synthesis process involves different sizes and physicochemical nature of particles in every synthesis stage. Equivalent quantities of each of purified pore-activated UiO-66 MOF, yet-to-be-purified pore-inactivated UiO-66 MOF, and reaction precursors of UiO-66 MOF give different deposition patterns when a well-dispersed aqueous droplet of these materials undergoes drying over substrates of varying stiffness and wettability. Yet-to-be-purified, pore-inactivated UiO-66 MOF nanoparticles undergo transport toward the droplet periphery, leading to a thick ring-like deposition at the dried droplet edge. Under appropriate drying conditions, such a deposit leads to desiccation-type mud-like reticular cracking. We study the origin of such ring-like deposits and cracks to understand how the surface charge density of UiO-66 particles controls their stability. We demonstrate that ZrOCl 2 salt trapped in a nonpurified pore-inactivated UiO-66 MOF moiety is the principal reason for ring-like deposit formation and subsequent cracking in its dried aqueous droplet edge. Qualitatively, we identified Lewis acid salts that are capable of acting as Bro̷nsted acid upon hydrolysis (like FeCl 3 , SnCl 2 , and ZrOCl 2 ), influence surface charge density and colloidal stability of dispersed UiO-66 MOF particles. As a result, immediate particle coagulation is avoided, so those travel to the droplet edge, forming ring-like deposition and subsequent cracking upon drying. Further, we show that crack patterns on such deposits are highly dependent on the stiffness and temperature of depositing substrates via a competition between axial and lateral strains at the deposit-substrate interface.