Adsorption enhancement of nitrogen gas by atomically heterogeneous nanospace of boron nitride.

In this study, porous boron nitride (p-BN) with hexagonal phase boron nitride (h-BN) pore walls was synthesized using high-temperature calcination. Negligible variation in pore-wall structure can be observed in powder X-ray diffraction (XRD) profiles and infrared (IR) spectra. However, a highly stable p-BN with a stable pore structure even at 973 K under the oxidative conditions is obtained when synthesized at higher than 1573 K under nitrogen gas flow. For p-BN, this stability is obtained by generating h-BN microcrystals. Nitrogen adsorption-desorption isotherms at 77 K provide type-IV features and typical adsorption-desorption hysteresis, which suggests micropore and mesopore formation. Moreover, adsorption-desorption isotherms of Ar at 87 K are measured and compared with those of nitrogen. The relative adsorbed amount of nitrogen ( i.e. , the amount of nitrogen normalized by that of Ar at each relative pressure or adsorption potential value) on p-BN is considerably larger than that on microporous carbon at low-pressure regions, which suggests the existence of strong adsorption sites on the p-BN surface. In fact, the relative number of adsorbed nitrogen molecules to that of Ar on p-BN is, at most, 150%-200% larger than that on microporous carbon for the same adsorption potential state. Furthermore, additional adsorption enhancement to nitrogen between P / P 0 = 10 -5 and 10 -3 can be observed for p-BN treated at 1673 K, which suggests the uniformly adsorbed layer formation of nitrogen molecules in the vicinity of a basal planar surface. Thus, unlike typical nanoporous sp 2 carbons, p-BN materials have the potential to enhance adsorption for certain gas species because of their unique surface state.