Slot-die coating large-area formamidinium-cesium perovskite film for efficient and stable parallel solar module.

Perovskite solar cells have emerged as one of the most promising thin-film photovoltaic (PV) technologies and have made a strong debut in the PV field. However, they still face difficulties with up-scaling to module-level devices and long-term stability issue. Here, we report the use of a room-temperature nonvolatile Lewis base additive, diphenyl sulfoxide(DPSO), in formamidinium-cesium (FACs) perovskite precursor solution to enhance the nucleation barrier and stabilize the wet precursor film for the scalable fabrication of uniform, large-area FACs perovskite films. With a parallel-interconnected module design, the resultant solar module realized a certified quasi-stabilized efficiency of 16.63% with an active area of 20.77 cm2 The encapsulated modules maintained 97 and 95% of their initial efficiencies after 10,000 and 1187 hours under day/night cycling and 1-sun equivalent white-light light-emitting diode array illumination with maximum power point tracking at 50°C, respectively.