Ethanol-induced Ni 2+ -intercalated Cobalt Organic Frameworks on Vanadium Pentoxide for Synergistically Enhancing the Performance of 3D-printed Micro-supercapacitors.

The synthesis of metal-organic framework (MOF) nanocomposites with high energy density and excellent mechanical strength is limited by the degree of lattice matching and crystal surface structure. In this study, dodecahedral ZIF-67 was synthesized uniformly on vanadium pentoxide nanowires. The influence of the coordination mode on the surface of ZIF-67 in ethanol was also investigated. Benefitting from the different coordination abilities of Ni 2+ , Co 2+ , and N atoms, spatially separated surface-active sites were created through metal-ion exchange. Furthermore, the incompatibility between the d8 electronic configuration of Ni 2+ and the three-dimensional (3D) structure of ZIF-67 afforded the synthesis of hollow structures by controlling the amount of Ni doping. The formation of NiCo-MOF@CoOOH@V 2 O 5 nanocomposites was confirmed using X-ray absorption fine structure analysis. The high performance of the obtained composite was illustrated by fabricating a 3D-printed micro-supercapacitor, exhibiting a high area specific capacitance of 585 mF cm -2 and energy density of 159.23 μWh cm -2 (at power density = 0.34 mW cm -2 ). The solvent/coordination tuning strategy demonstrated in this study provides a new direction for the synthesis of high-performance nanomaterials for electrochemical energy storage applications. This article is protected by copyright. All rights reserved.