Fs Laser Patterning of Amorphous As 2 S 3 Thin Films.

Claudia MihaiFlorin JipaGabriel SocolAdrian E KissMarian ZamfirescuAlin Velea
Published in: Materials (Basel, Switzerland) (2024)
This study investigates the morphological changes induced by femtosecond (fs) laser pulses in arsenic trisulfide (As 2 S 3 ) thin films and gold-arsenic trisulfide (Au\As 2 S 3 ) heterostructures, grown by pulsed laser deposition (PLD). By means of a direct laser writing experimental setup, the films were systematically irradiated at various laser power and irradiation times to observe their effects on surface modifications. AFM was employed for morphological and topological characterization. Our results reveal a clear transition threshold between photoexpansion and photoevaporation phenomena under different femtosecond laser power regimes, occurring between 1 and 1.5 mW, irrespective of exposure time. Notably, the presence of a gold layer in the heterostructure minimally influenced this threshold. A maximum photoexpansion of 5.2% was obtained in As 2 S 3 films, while the Au\As 2 S 3 heterostructure exhibited a peak photoexpansion of 0.8%. The study also includes a comparative analysis of continuous-wave (cw) laser irradiation, confirming the efficiency of fs laser pulses in inducing photoexpansion effects.
Keyphrases
  • high speed
  • room temperature
  • gene expression
  • sensitive detection
  • dna methylation
  • radiation therapy
  • high resolution
  • single cell
  • atomic force microscopy
  • gold nanoparticles
  • reduced graphene oxide