Fabrication of Mn-Doped SrTiO 3 /Carbon Fiber with Oxygen Vacancy for Enhanced Photocatalytic Hydrogen Evolution.

With carbon fiber, it is difficult to load semiconductor photocatalysts and easy to shed off thanks to its smooth surface and few active groups, which has always been a problem in the synthesis of photocatalysts. In the study, SrTiO 3 nanoparticles were loaded onto the Tencel fibers using the solvothermal method, and then the Tencel fibers were carbonized at a high temperature under the condition of inert gas to form carbon fibers, thus SrTiO 3 @CF photocatalytic composite materials with solid core shell structure were prepared. Meanwhile, Mn ions were added into the SrTiO 3 precursor reagent in the solvothermal experiment to prepare Mn-doped Mn-SrTiO 3 @CF photocatalytic composite material. XPS and EPR tests showed that the prepared Mn-SrTiO 3 @CF photocatalytic composite was rich in oxygen vacancies. The existence of these oxygen vacancies formed oxygen defect states (VOs) below the conduction band, which constituted the capture center of photogenerated electrons and significantly improved the photocatalytic activity. The photocatalytic hydrogen experimental results showed that the photocatalytic hydrogen production capacity of Mn-SrTiO 3 @CF composite material with 5% Mn-doped was six times that of the SrTiO 3 @CF material, and the doping of Mn ions not only promoted the red shift of the light absorption boundary and the extension to visible light, but also improved the separation and migration efficiency of photocarriers. In the paper, the preparation method solves the difficulty of loading photocatalysts on CF and provides a new design method for the recycling of catalysts, and we improve the hydrogen production performance of photocatalysts by Mn-doped modification and the introduction of oxygen vacancies, which provides a theoretical method for the practical application of hydrogen energy.