Alkaline all iron redox flow battery with a polyethylene/poly(styrene- co -divinylbenzene) interpolymer cation-exchange membrane.

This work describes the suitability of a polyethylene styrene-DVB based interpolymer cation exchange membrane for use in a highly alkaline redox flow battery (RFB) with a [Fe(TEA)OH] 2- /[Fe(TEA)OH] - and Fe(CN) 6 3- /Fe(CN) 6 4- redox couple. The alkaline stability of the membrane for 1440 h was evaluated in 5 N NaOH containing a 200 mM Fe(CN) 6 3- /Fe(CN) 6 4- redox couple. It was assessed according to the changes in the electrochemical and physicochemical properties. The performance of the membrane was evaluated over 40 charge-discharge cycles at a current density of 5 mA cm -2 current in a designed RFB cell. The obtained average coulombic efficiency (CE) was 92%, energy efficiency (EE) was 75%, voltage efficiency (VE) was 82% and volumetric efficiency was 34%. Under identical experimental conditions, the values of CE, EE, and VE for Nafion®-112 were 99%, 75%, and 76%, respectively. These results indicate the suitability of the polyethylene styrene-DVB based interpolymer cation exchange membrane for use in an alkaline RFB.