Preparation and Characterization of Narrow Size Distribution PMSQ Microspheres for High-Frequency Electronic Packaging.

Polymethylsilsesquioxane (PMSQ) has become a kind of widely studied filler used in the electronic circuit board substrates due to its organic-inorganic hybrid structure, low dielectric constant, and good thermal stability, among other factors. Herein, the PMSQ microspheres were prepared by a two-step acid-base-catalyzed sol-gel method; the influences of reaction conditions including the ratio of water/methyltrimethoxysilane (MTMS), reaction temperature, concentration of the catalyst, and stirring time were systematically investigated; and the optimized reaction condition was then obtained towards a narrow particle size distribution and good sphericity. The microstructure of PMSQ microspheres was analyzed by the infrared spectrum and X-ray diffraction (XRD), which indicated that the as-prepared PMSQ had a ladder-dominant structure. The thermogravimetric analysis (TGA) demonstrated an excellent thermal stability of as-prepared PMSQ microspheres. More specifically, the dielectric constants at high frequency (1~20 GHz) of as-prepared PMSQ microspheres were measured to be about 3.7, which turned out a lower dielectric constant compared to SiO2 powder (≈4.0). This study paves the way to further improve the performance of the electronic circuit board substrates for the application of high-frequency electronic packaging.