Al 2 O 3 /WS 2 Surface Layers Produced on the Basis of Aluminum Alloys for Applications in Oil-Free Kinematic Systems.

The article presents the results of an aluminum oxide layer doped with monolayer 2H tungsten disulphide (Al 2 O 3 /WS 2 ) for applications in oil-free kinematic systems. The results concern the test carried out on the pneumatic actuator operational test stand, which is the actual pneumatic system with electromagnetic control. The cylinders of actuators are made of Ø 40 mm aluminum tube of EN-AW-6063 aluminum alloy which is used in the manufacture of commercial air cylinder actuators. The inner surfaces of the cylinder surfaces were covered with an Al 2 O 3 /WS 2 oxide layer obtained by anodic oxidation in a three-component electrolyte and in the same electrolyte with the addition of tungsten disulfide 2H-WS 2 . The layers of Al 2 O 3 and Al 2 O 3 /WS 2 obtained on the inner surface of the pneumatic actuators were combined with a piston ring made of polytetrafluoroethylene with carbon (T5W) material and piston seals made of polyurethane (PU). The cooperation occurred in the conditions of technically dry friction. After the test was carried out, the scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS) analysis of the surface of the cylinder bearing surfaces and piston seals of the pneumatic cylinders was performed. The analysis revealed the formation of a sliding film on the cylinder surface modified with tungsten disulfide, as well as on the surface of wiper seals. Based on the SEM/EDSM tests, it was also found that the modification of the Al 2 O 3 layer with tungsten disulfide contributed to the formation of a sliding film with the presence of WS 2 lubricant, which translated into smooth cylinder operation during 180 h of actuator operation. The cylinder with the unmodified layer showed irregular operation after approximately 70 h thereof.