Biomimetic 3D-printed PCL scaffold containing a high concentration carbonated-nanohydroxyapatite with immobilized-collagen for bone tissue engineering: enhanced bioactivity and physicomechanical characteristics.

Ali MoghaddaszadehHadi SeddiqiNajmeh NajmoddinSonia Abbasi RavasjaniJenneke Kleine-Nulend
Published in: Biomedical materials (Bristol, England) (2021)
A challenging approach of three-dimensional (3D)-biomimetic scaffold design for bone tissue engineering is to improve scaffold bioactivity and mechanical properties. We aimed to design and fabricate 3D-polycaprolactone (PCL)-based nanocomposite scaffold containing a high concentration homogeneously distributed carbonated-nanohydroxyapatite (C-nHA)-particles in combination with immobilized-collagen to mimic real bone properties. PCL-scaffolds without/with C-nHA at 30%, 45%, and 60% (wt/wt) were 3D-printed. PCL/C-nHA60%-scaffolds were surface-modified by NaOH-treatment and collagen-immobilization. Physicomechanical and biological properties were investigated experimentally and by finite-element (FE) modeling. Scaffold surface-roughness enhanced by increasing C-nHA (1.7 - 6.1-fold), but decreased by surface-modification (0.6-fold). The contact angle decreased by increasing C-nHA (0.9 - 0.7-fold), and by surface-modification (0.5-fold). The zeta potential decreased by increasing C-nHA (3.2-9.9-fold). Average elastic modulus, compressive strength, and reaction force enhanced by increasing C-nHA and by surface-modification. FE modeling revealed that von Mises stress distribution became less homogeneous by increasing C-nHA, and by surface-modification. Maximal von Mises stress for 2% compression strain in all scaffolds did not exceed yield stress for bulk-material. 3D-printed PCL/C-nHA60% with surface-modification enhanced pre-osteoblast spreading, proliferation, collagen deposition, alkaline phosphatase activity, and mineralization. In conclusion, a novel biomimetic 3D-printed PCL-scaffold containing a high concentration C-nHA with surface-modification was successfully fabricated. It exhibited superior physicomechanical and biological properties, making it a promising biomaterial for bone tissue engineering.
Keyphrases