Effect of fluorination of naphthalene diimide-benzothiadiazole copolymers on ambipolar behavior in field-effect transistors.

Cunbin AnHanna MakowskaBenlin HuRuomeng DuanWojciech PisulaTomasz MarszalekMartin Baumgarten
Published in: RSC advances (2018)
Two naphthalene diimide (NDI)-benzothiadiazole (BT) based conjugated polymers with high molecular weight, P1 and P2, were synthesized by introducing F atoms to modulate the electron-donating ability of the BT moiety. 3-Decyl-pentadecyl branched alkyl side chains were employed and expected to improve the molecular organization and device performance. Both polymers have excellent solubility in common organic solvents. UV-vis-NIR absorption and cyclic voltammetry indicate that the maximum absorption wavelength of P2 is blue-shifted and the HOMO energy level of P2 is decreased in comparison with P1. Two dimensional wide angle X-ray scattering of thin films revealed a similar organization of both polymers. A less balanced transport in field-effect transistors with increased electron mobility of 0.258 cm 2 V -1 s -1 and lowered hole transport of 2.4 × 10 -3 cm 2 V -1 s -1 was found for P2. Polymer devices of P1 exhibited a balanced ambipolar transport, with a hole mobility of 0.073 cm 2 V -1 s -1 and electron mobility of 0.086 cm 2 V -1 s -1 .
Keyphrases
  • solar cells
  • high resolution
  • electron microscopy
  • photodynamic therapy
  • ionic liquid
  • perovskite solar cells
  • single cell
  • computed tomography
  • drug release
  • dual energy