Cross-Link Density, Mechanical and Thermal Properties of Chloroprene Rubber Cross-Linked with Silver(I) Oxide.

The purpose of this work was to cross-link chloroprene rubber (CR) with silver(I) oxide (Ag 2 O) and to investigate the properties of the obtained vulcanizates. Silver(I) oxide was chosen as an alternative to zinc oxide (ZnO), which is part of the standard CR cross-linking system. The obtained results show that it is possible to cross-link chloroprene rubber with silver(I) oxide. This is evidenced by the determined vulcametric parameters, equilibrium swelling and elasticity constants. As the Ag 2 O content in the composition increases, the cross-link density of the vulcanizates also increases. However, the use of 1 phr of Ag 2 O is insufficient to obtain a suitably extensive network. Exclusively, the incorporation of 2 phr of Ag 2 O results in obtaining vulcanizates with great cross-link density. The obtained compositions are characterized by good mechanical properties, as evidenced by high tensile strength. The performed thermal analyses-differential scanning calorimetry (DSC) and thermogravimetry (TGA) allowed us to determine the course of composition cross-linking, but also to determine changes in their properties during heating. The results of the thermal analysis confirmed that CR can be cross-linked with Ag 2 O, and the increasing amount of oxide in the composition increases the degree of cross-linking of vulcanizates. However, the amount of Ag 2 O in the composition does not affect the processes occurring in the heated vulcanizate.