Controlling the Superconductivity of Nb 2 Pd x S 5 via Reversible Li Intercalation.

Mahmoud ElgamlSunita DeyJiayi CenMaxim AvdeevDavid O ScanlonClare P GreySimon J Clarke
Published in: Inorganic chemistry (2024)
The Nb 2 Pd x S 5 ( x ≈ 0.74) superconductor with a T c of 6.5 K is reduced by the intercalation of lithium in ammonia solution or electrochemically to produce an intercalated phase with expanded lattice parameters. The structure expands by 2% in volume and maintains the C 2/ m symmetry and rigidity due to the PdS 4 units linking the layers. Experimental and computational analysis of the chemically synthesized bulk sample shows that Li occupies triangular prismatic sites between the layers with an occupancy of 0.33(4). This level of intercalation suppresses the superconductivity, with the injection of electrons into the metallic system observed to also reduce the Pauli paramagnetism by ∼40% as the bands are filled to a Fermi level with a lower density of states than in the host material. Deintercalation using iodine partially restores the superconductivity, albeit at a lower T c of ∼5.5 K and with a smaller volume fraction than in fresh Nb 2 Pd x S 5 . Electrochemical intercalation reproduces the chemical intercalation product at low Li content (<0.4) and also enables greater reduction, but at higher Li contents (≥0.4) accessed by this route, phase separation occurs with the indication that Li occupies another site.
Keyphrases
  • ion batteries
  • solid state
  • signaling pathway
  • gold nanoparticles
  • magnetic resonance imaging
  • magnetic resonance
  • label free
  • anaerobic digestion