Ferrocene-Boosted Nickel Sulfide Nanoarchitecture for Enhanced Alkaline Water Splitting.

Enhanced electrocatalysts that are cost-effective, durable, and derived from abundant resources are imperative for developing efficient and sustainable electrochemical water-splitting systems to produce hydrogen. Therefore, the design and development of non-noble-based catalysts with more environmentally sustainable alternatives in efficient alkaline electrolyzers are important. This work reports ferrocene (Fc)-incorporated nickel sulfide nanostructured electrocatalysts (Fc-NiS) using a one-step facile solvothermal method for water-splitting reactions. Fc-NiS exhibited exceptional electrocatalytic activity under highly alkaline conditions, evident from its peak current density of 345 mA cm -2 , surpassing the 153 mA cm -2 achieved by the pristine nickel sulfide (NiS) catalysts. Introducing ferrocene enhances electrical conductivity and facilitates charge transfer during water-splitting reactions, owing to the inclusion of iron metal. Fc-NiS exhibits a very small overpotential of 290 mV at 10 mA cm -2 and a Tafel slope of 50.46 mV dec -1 , indicating its superior charge transfer characteristics for the three-electron transfer process involved in water splitting. This outstanding electrocatalytic performance is due to the synergistic effects embedded within the nanoscale architecture of Fc-NiS. Furthermore, the Fc-NiS catalyst also shows a stable response for the water-splitting reactions. It maintains a steady current density with an 87% retention rate for 25 hours of continuous operation, indicating its robustness and potential for prolonged electrolysis processes.